The market for zirconia dental materials is further expanded

Zirconia ceramics have performance advantages over other dental materials.

The materials for dental restoration mainly include: resin, common alloy (nickel chromium, etc.), precious metal alloy (gold platinum, etc.) and ceramics (zirconia and alumina, etc.).

From the five dimensions of “Aesthetic, Biological performance, stability, mechanical properties and cost”, zirconia ceramic materials have many advantages over other materials.

Zirconia materials are widely used in dental restorations. At present, the main methods of dental restoration can be divided into the following three categories according to the degree of tooth damage:
(1) Inlay repair, suitable for partial damage of the teeth, filled with inlays to protect and repair the teeth. Commonly used inlay repair materials are mainly resin, metal and ceramics;
(2) Crown repair, suitable for teeth defects, or lesions, but the roots are still in the situation. Commonly used crown materials are alloys, porcelain and all-ceramic;
(3)  Dental restoration, suitable for missing teeth, or extracted teeth.


Performance comparison of different dental materials


efni

Fagurfræði

Biological   performance

Stöðugleiki

Mechanical   performance

Kostnaður

Common   alloy

Léleg

Léleg

Betri

Betri

Lægst

Precious   metal alloy

Léleg

best

Betri

Betri

Æðri

Plastefni

Betri

Betri

Léleg

Léleg

neðri

Other ceramics

Betri

Betri

Betri

Léleg

Æðri

Zirconia

best

Betri

best

Betri

Æðri

 

Some Vsmile dental zirconia block parameters

 HappyZir for Full Contour

Property

Unit

HappyZir+Value

ISO   Requirement

Bulk   Density

g / cm3

6.085 ~ 6.095

≥   6.00 (ISO 13356)

ZrO2 +   HfO2 + Y2O3

%

>   99.5

>   99

ZrO2

%

91.6

N / A

Y2O3           

%

5.9-6

4.5   - 6

HfO2

%

3

≤   5

Al2O3

%

<   0.15

<   0.5

Other   Oxides

%

<   0.2

<   0.5

Mean   Linear Intercept Distance

µm

0.25   ± 0.05

≤   0.4 (ISO 13356)

Biaxial   Flexure Strength

MPa

1000   ± 100

≥   500

CTE


10   x 10-6(25~900ºC)

N / A

Final   Sintered Hardness

HV10

1200 ~ 1300

N / A

Pre-Sintered   Hardness

HV10

60 ~ 70

N / A

Gegnsæi

1-CR%(1.0mm)

41 ~ 45

N / A